Thank you Rury, that is kind. And I am pleased it helps you Nick, if any specific questions arise I will do my best to answer them for you. The car its self has languished in storage for the past couple of years as I have been through some major upheaval in my life. I recently collected it and brought it back down to my new home in Wellington, hopefully I can start working on it again soon, I will update the thread once that happens.
I think I mainly used 1.6mm 5005, I would have annealed before working and it work hardens quite quickly, some of the structural panels will have been 1.8mm and there was probably a little 1.2mm used in some places.
I think I mainly used 1.6mm 5005, I would have annealed before working and it work hardens quite quickly, some of the structural panels will have been 1.8mm and there was probably a little 1.2mm used in some places.