17-01-2022, 06:53 PM
Depends what you are stripping Hugh.
If it is alloy I would strongly advise against chemicals and use soda blasting.
If it is steel ,chemical stripping is OK I take the item for dipping locally having found modern strippers one can buy to be ineffective.